It is easy to return T6 to T0. Just heat it up until it will char wood, and let it cool. You can treat local areas by torch, or use an oven. Cold working will restore the hardness, so sometimes it must be re-annealed. You can repeat this indefinitely, turning any metal shape into any other shape if necessary.
|